Liaparo tsa galvalume tsa Zn55Al1.6Si li 'nile tsa sebelisoa haholo libakeng tse ngata tse kang indasteri ea likoloi, kaho ea likepe, indasteri ea mechine, joalo-joalo, ka lebaka la ts'ebetso ea eona e ntle ea ho thibela ho senya ho feta ea Zinc, empa hape le ka theko e tlaase ( theko ea Al e tlase ho feta ea Zn hajoale). Lifate tse sa tloaelehang tse kang La li ka sitisa kholo ea kholo le ho eketsa ho khomarela, ka hona li hiriloe ho sireletsa litšepe le tse ling. tšepe alloys khahlano le oxidation le corrosion. Leha ho le joalo, ho na le lingoliloeng tse seng kae feela tse hatisitsoeng mabapi le kopo ea La ka ho chesa galvalume barbotage, 'me pampiring ena liphello tsa La phaella ka ho re ho hanyetsa ha kutu ea ho chesa galvalume barbotage ba ile ba fuputswa.

Teko

[1] Ho qoela ho chesang

Liaparo tsa alloy tsa Zn-Al-Si-La tse chesang tse chesang tse nang le 0,0.02wt.%, 0.05wt.%, 0.1wt.% le 0.2wt.% La li ne li sebelisoa ho Ф 1 mm terata ea tšepe e bonolo. Ts'ebetso e ne e le ka tsela e latelang: ho hloekisa ho tlosa mafome le ho tlotsa ka leqhubu la supersonic (55 °C) → ho hloekisa ka metsi → fluxing(85 °C)→ho omisa (100~200 °C) ho qoelisoa ho chesang (640~670 °C, 3-5 s).

[2]Teko ea ho theola boima ba 'mele

Teko ea ho theola boima ba 'mele e ile ea lekanyetsoa ka tlhahlobo ea koporo e potlakileng ea acetic acid ea letsoai (CASS) le liteko tsa ho qoelisoa tsa kutu tse entsoeng ka phaposing ea ho fafatsa letsoai le tharollo ea NaCl ea 3.5%. Ka mor'a liteko, lihlahisoa tse senyang li ne li tlosoa ka mekhoa ea mechine, li hlatsuoa ka metsi a phallang, ebe li omisitsoe ke moea o batang oa ho phatloha le ho lahleheloa ke boima ba 'mele ho lekanngoa ka tekanyo ea elektronike. Maemong ana ka bobeli, tse tharo parallisampole tsa lel li entsoe ho fumana liphetho tse nepahetseng haholoanyane. Nako ea teko e ne e le 120 h bakeng sa tlhahlobo ea CASS le lihora tse 840 bakeng sa tlhahlobo ea ho qoelisoa.

[3] Teko ea electrochemical

Teko ea electrochemical e entsoe ke IM6e electrochemical work station e fanoeng ke Jeremane, e nka poleiti ea platinum e le electrode ea counter, saturated calomel electrode e le electrode ea litšupiso, le terata ea tšepe ea Zn-Al-Si-La e kenngoeng ka ho chesa e le electrode e sebetsang. Mokhoa o senyang e ne e le tharollo ea NaCl ea 3.5%. Sebaka se ka holimo se neng se pepesehetse tharollo ea teko e ne e le 1cm2. Electrochemical impedance spectroscopy (EIS) litekanyo li ile tsa etsoa ka mefuta ea maqhubu a tloha ho 10 kHz ho ea ho 10 mHz, bophara ba pontšo ea sinusoidal voltage e ne e le 10 mV (rms) . ho isa ho 70 mV, sekhahla sa ho skena e ne e le 70 mV/s. Maemong ana ka bobeli, teko ha ea ka ea qala ho fihlela matla a kutu a lula a tsitsitse (phapang e ka tlase ho 1 mV ka 5 min).

[4]Lithuto tsa SEM le XRD

Li-surface morphologies tsa lisampole li ile tsa hlahlojoa ke SSX-550 scanning electron microscope (SEM) ka mor'a liteko tsa ho bola ka phaposing ea spray ea letsoai le tharollo ea 3.5% ea NaCl. Lihlahisoa tsa kutu tse entsoeng holim'a lisampole ka har'a sesepa sa letsoai le tharollo ea 3.5% ea NaCl e ile ea lekoa ho sebelisoa PW-3040160 X-ray diffraction (XRD).

Liphetho le puisano

[1] Ho hanyetsa kutu
[1.1] Ho theola boima ba 'mele
Setšoantšo sa 1 se bontša liphello tsa liteko tsa ho lahleheloa ke boima ba 'mele ka har'a khabinete ea spray ea letsoai le tharollo ea 3.5% ea NaCl. Sekhahla sa kutu ea lisampole maemong ana ka bobeli se fokotsehile pele ka ho eketseha ha litaba tsa La ho fihla ho 0.05wt.% ebe se eketseha ka litaba tsa La tse ntseng li eketseha. Ka hona, khanyetso e ntle ka ho fetisisa ea kutu e bile teng ka har'a liphahlo tse nang le 0.05wt.%La. Ho ile ha fumanoa hore nakong ea teko ea ho qoelisoa, mafome a khubelu a fumanoe pele ho 0wt.% La coating surface ka 3.5% NaCl tharollo, leha ho le joalo, ho fihlela tlhahlobo ea ho qoelisoa e fela, ho ne ho se na mafome a khubelu holim'a 0.05wt.% La ho roala holim'a metsi. .

2.1.2 Teko ea electrochemical

Setšoantšo sa 2 se bontša li-curve tse fokolang tsa polarization bakeng sa liaparo tsa alloy Zn-Al-Si-La ka tharollo ea 3.5% ea NaCl. Ho ka bonoa hore sebopeho sa li-curve tse fokolang tsa polarization li bonts'itse liphapang tse fokolang, mme ts'ebetso ea kutu ea mefuta eohle ea liaparo tsa alloy e ne e laoloa ke karabelo ea cathodic. Liphetho tse loketseng tsa Tafel tse thehiloeng ho li-curve tse fokolang tsa polarization ho Fig.2 li hlahisoa ho Lethathamo la 1. Ho tšoana le teko ea ho lahleheloa ke boima ba 'mele, ho ile ha boela ha fumanoa hore ho hanyetsa ha kutu ea ho roala ha galvalume ho ka ntlafatsoa ka ho eketsa ho honyenyane ha La le bonyane. sekhahla sa kutu se fumanoe ka 0.05wt.%La.

Setšoantšo sa 3 se emela litšoantšo tsa Nyquist tse tlalehiloeng bakeng sa ho roala ka mefuta e fapaneng ea ho eketsa La ho pepesehela tharollo ea 3.5% ea NaCl bakeng sa 0.5 h. Maemong 'ohle, ho ne ho e-na le li-arcs tse peli tse bolelang hore ho na le linako tse peli tse tsitsitseng. E hlahang ka maqhubu a phahameng e ne e emela tšobotsi ea dielectric ea motsoako oa alloy, ha e fokolang e ne e tšoana le ea substrate e bonolo ea tšepe e ka har'a masoba (ke hore Coating defects). Ha tlatsetso ea La e ntse e eketseha, bophara ba maqhubu a phahameng a arc bo ile ba eketseha, phello ena e ile ea bonahala haholoanyane tabeng ea Zn55Al1.6Si0.05La alloy coating. Ka ho eketseha ha litaba tsa La, leha ho le joalo, bophara ba maqhubu a phahameng a arc bo fokotsehile ka tsela e fapaneng. Ho sa le joalo, setsi sa li-arcs tsohle se itšetlehile ka quadrant ea bone, e bontšang hore phello ea ho hasana e etsahetse ka holim'a electrode. lihlopha tse ling tsa lipatlisiso.