Kafukufuku wa Corrosion Resistance of Hot dipped Galvalume Coating

Zn55Al1.6Si galvalume zokutira zoviikidwa pamoto zakhala zikugwiritsidwa ntchito kwambiri m'mafakitale ambiri monga magalimoto, zomanga zombo, makina opangira makina ndi zina, chifukwa osati chifukwa chakuchita bwino kwa anti-zinc kuposa zokutira kwa Zinc, komanso chifukwa chotsika mtengo. mtengo wa Al ndi wotsika kuposa wa Zn pakadali pano). Zosowa zapadziko lapansi monga La zimatha kulepheretsa kukula ndikuwonjezera kumamatira, motero adagwiritsidwa ntchito kuteteza zitsulo ndi zina. zitsulo ma aloyi motsutsana ndi oxidation ndi dzimbiri. Komabe, pali mabuku ochepa okha omwe amafalitsidwa pakugwiritsa ntchito La mu ❖ kuyanika koviika kwa galvalume, ndipo mu pepalali zotsatira za La kuwonjezera pa kukana dzimbiri za ❖ kuyanika galvalume yotentha anafufuzidwa.

experimental

[1] Kutentha kwamoto

Zn-Al-Si-La zokutira zotsekemera zotentha zokhala ndi 0,0.02wt.%, 0.05wt.%, 0.1wt.% ndi 0.2wt.% La zidagwiritsidwa ntchito pa Ф 1 mm waya wofatsa wachitsulo. Njirayi inali motere: kuyeretsa kuchotsa dzimbiri ndi kupaka mafuta ndi mafunde apamwamba (55 °C)→kuyeretsa ndi madzi→ kusuntha(85 °C)→kuyanika (100~200 °C) kuviika kotentha(640~670 °C, 3 ndime 5).

[2]Kuyesa kuchepa thupi

Kuyeza kulemera kwake kunayesedwa ndi kuyesa kwa mchere wa mchere wa acetic acid (CASS) ndi kumiza kwa dzimbiri komwe kumachitika mu chipinda chopopera mchere ndi 3.5% NaCl solution. Pambuyo pa mayeserowo, zowononga zowonongeka zimachotsedwa ndi njira zamakina, zotsukidwa ndi madzi othamanga, kenako zowumitsidwa ndi mpweya wozizira komanso kuchepa kwa thupi kumayesedwa ndi magetsi. Muzochitika zonsezi, atatu parallel zitsanzo zinapangidwa kuti apeze zotsatira zolondola. Nthawi yoyesera inali 120 h ya mayeso a CASS ndi 840 h yoyezetsa kumizidwa.

[3] Mayeso a Electrochemical

Kuyesa kwa electrochemical kunachitika ndi IM6e electrochemical work station yoperekedwa ndi Germany, kutenga mbale ya platinamu ngati ma electrode, ma elekitirodi a calomel odzaza ngati maelekitirodi, ndi zokutira zoviikidwa za Zn-Al-Si-La waya wachitsulo wofewa ngati electrode yogwira ntchito. Sing'anga yowonongeka inali yankho la 3.5% la NaCl. Malo omwe adawonetsedwa ndi yankho la mayeso anali 1cm2. Miyezo ya Electrochemical impedance spectroscopy (EIS) inkachitika ndi kuchuluka kwa ma frequency kuchokera ku 10 kHz mpaka 10 mHz, m'lifupi mwa sinusoidal voltage siginecha inali 10 mV (rms) . mpaka 70 mV, mlingo wojambulira unali 70 mV/s. Pazochitika zonsezi, kuyesa sikunayambe mpaka mphamvu ya dzimbiri ikhalebe yokhazikika (kusiyana kwa osachepera 1 mV mu 5 min).

[4] Maphunziro a SEM ndi XRD

Ma morphologies apamwamba a zitsanzozo adawunikidwa ndi SSX-550 scanning electron microscope (SEM) pambuyo pa kuyesa kwa dzimbiri mu chipinda chopopera mchere ndi 3.5% NaCl solution. Zinthu zowonongeka zomwe zinapangidwa pamwamba pa zitsanzo za mchere wa mchere ndi 3.5% NaCl yankho anayesedwa pogwiritsa ntchito PW-3040160 X-ray diffraction (XRD).

Zotsatira ndi zokambirana

[1] Kukana kwa dzimbiri
[1.1] Kuchepetsa thupi
Chithunzi 1 chikuwonetsa zotsatira za mayeso ochepetsa thupi mu kabati yopopera mchere ndi 3.5% NaCl solution. Kuchuluka kwa dzimbiri kwa zitsanzo m'magawo onse awiriwo kudatsika koyamba ndikuwonjezeka kwa La zomwe zili mpaka 0.05wt.% kenako ndikuwonjezeka ndikuwonjezeka kwa La zomwe zili. Choncho, kukana kwa dzimbiri kwabwino kwambiri kunachitikira mu zokutira zomwe zili ndi 0.05wt.%La. Zinapezeka kuti pakuyezetsa kumizidwa, dzimbiri lofiira linapezeka koyambirira pa 0wt.% La yokutira pamwamba pa 3.5% NaCl yankho, komabe, mpaka kuyesa kumiza kutha, panalibe dzimbiri lofiira pa 0.05wt.% La zokutira pamwamba. .

2.1.2 Mayeso a Electrochemical

Chithunzi 2 chikuwonetsa ma curve ofooka a polarization a Zn-Al-Si-La alloy zokutira mu 3.5% NaCl yankho. Zitha kuwoneka kuti mawonekedwe a ma curve ofooka a polarization adawonetsa kusiyana pang'ono, ndipo njira ya dzimbiri yamitundu yonse ya zokutira za aloyi idayendetsedwa ndi cathodic reaction. Zotsatira zoyenerera za Tafel zochokera ku zofooka zofooka za polarization mu Fig.2 zimaperekedwa mu Table 1. Mofanana ndi kuyesa kulemera kwa thupi, kunapezekanso kuti kukana kwa chiwombankhanga cha chophimba cha galvalume chikhoza kusinthidwa ndi kuwonjezera pang'ono kwa La ndi osachepera. kuchuluka kwa dzimbiri kunapezedwa ndi 0.05wt.%La.

Fig.3 imayimira zithunzi za Nyquist zolembedwa kuti zokutira ndi kuchuluka kosiyana kwa La kuwonjezera pa 3.5% NaCl yankho kwa 0.5 h. Muzochitika zonse, panali ma arcs awiri omwe amatanthawuza zokhazikika ziwiri. Yowonekera pafupipafupi imayimira mawonekedwe a dielectric a zokutira aloyi, pomwe yotsika pafupipafupi imafanana ndi gawo lapansi lachitsulo chocheperako m'zibowo (ie Kupaka zolakwika). Pamene kuwonjezera kwa La kumawonjezeka, kuchuluka kwa ma frequency arc arc kumawonjezeka, izi zimamveka bwino ngati Zn55Al1.6Si0.05La zokutira alloy. Ndikuchulukirachulukira kwa zomwe zili mu La, komabe, kuchuluka kwa ma frequency arc kunachepa mosiyanasiyana. Panthawiyi, pakati pa ma arcs onse adatsamira ku quadrant yachinayi, kusonyeza kuti kufalikira kunachitika pamtunda wa electrode. magulu ena ofufuza.